Cooling, Scattering, and Recombination-The Role of the Material Quality for the Physics of Tin Halide Perovskites

Kahmann, S., Shao, S. & Loi, M. A., Aug-2019, In : Advanced Functional Materials. 29, 35, 8 p., 1902963.

Research output: Contribution to journalArticleAcademicpeer-review

Tin-based perovskites have long remained a side topic in current perovskite optoelectronic research. With the recent efficiency improvement in thin film solar cells and the observation of a long hot carrier cooling time in formamidinium tin iodide (FASnI(3)), a thorough understanding of the material's photophysics becomes a pressing matter. Since pronounced background doping can easily obscure the actual material properties, it is of paramount importance to understand how different processing conditions affect the observed behavior. Using photoluminescence spectroscopy, thin films of FASnI(3) fabricated through different protocols are therefore investigated. It is shown that hot carrier relaxation occurs much faster in highly p-doped films due to carrier-carrier scattering. From high quality thin films, the longitudinal optical phonon energy and the electron-phonon coupling constant are extracted, which are fundamental to understanding carrier cooling. Importantly, high quality films allow for the observation of a previously unreported state of microsecond lifetime at lower energy in FASnI(3), that has important consequences for the discussion of long lived emission in the field of metal halide perovskites.

Original languageEnglish
Article number1902963
Number of pages8
JournalAdvanced Functional Materials
Volume29
Issue number35
Publication statusPublished - Aug-2019

    Keywords

  • hot carriers, metal halide perovskites, photophysics, spectroscopy, SOLAR-CELLS, LEAD, DYNAMICS

View graph of relations

Download statistics

No data available

ID: 97360103